Dependence of Melt Behavior of Star Polystyrene/POSS Composites on the Molecular Weight of Arm Chains.
作者：Haiying Tan, Jun Zheng, Donghua Xu, Dong Wan, Jian Qiu, and Tao Tang*.
關(guān)鍵字：///
論文來(lái)源：期刊
具體來(lái)源：J. Phys. Chem. B 2014, 118, 5229?5239.
發(fā)表時(shí)間：2014年
Rheological behavior of three-arm and six-arm star polystyrene (SPS) with
a small amount of polyhedral oligosilsesquioxane (POSS) was studied. Both linear
oscillatory frequency sweep and steady state shear results of SPS/POSS composites
showed the reduction of melt viscosity in the unentangled SPS matrix and the increase of
viscosity in the entangled SPS matrix. In particular, when molecular weight of the arm
(Ma) of SPS was smaller than the critical molecular weight for entanglement (Mc) of PS,
the melt viscosity of SPS/POSS composites with low content of POSS was lower than that
of pure SPS. The abnormal phenomenon of reduced melt viscosity in SPS/POSS
composites was in coincidence with the melt viscosity behavior of SPS/C60 composites
reported in our previous work (Soft Matter 2013, 9, 6282?6290), although the diameters
of two nanoparticles and their interaction with SPS matrix were different. A possible
mechanism behind the melt viscosity behavior was discussed. Furthermore, the time?
temperature superposition principle (TTS) was applied in SPS and SPS/POSS
composites. The Cox?Merz empirical relationship was verified to be valid for SPS/POSS composites when the content of
POSS was low (1 wt %).