164. Mild synthesis of environment-friendly thermoplastic triblock copolymer elastomers through combination of ring-opening and RAFT polymerization
作者：Chu Fang, Xuehui Wang,* Xuesi Chen and Zhigang Wang*
關鍵字：Triblock copolymer, elastomer, PLA-b-PI-b-PLA
論文來源：期刊
具體來源：Polym. Chem., 2019, 10, 3610-3620
發(fā)表時間：2019年
Structurally well-defined environment-friendly thermoplastic triblock copolymer elastomers, polylactideblock-polyisoprene-block-polylactide (PLA-b-PI-b-PLA), were synthesized by a creative mild method, which combines ring-opening polymerization (ROP) and subsequent reversible addition-fragmentation chain transfer (RAFT) polymerization. A PLA-based macromolecular chain transfer agent (PLA-CTA) was first synthesized by ROP from the monomer L-lactide (LA) initiated by a specifically prepared di-hydroxylterminated chain transfer agent 1,4-phenylenebis(methylene)bis(2-hydroxyethyl) dicarbonotrithioate (PMHD) with 1,8-diazabicyclo[5.4.0]undec-7-ene (DBU) serving as a nonmetallic catalyst. Then, a series of PLA-b-PI-b-PLA triblock copolymers were synthesized via RAFT polymerization by using the PLA-CTA and isoprene with di-tert-butyl peroxide (DTBP) as the initiator. In these triblock copolymers, PLA end blocks were dispersed as hard microdomains in the rubbery PI matrix as revealed by two distinct glass transition temperatures from differential scanning calorimetry and by typical phase-separated morphologies from transmission electron microscopy observation. By tuning the molecular mass of the PI midblock, these triblock copolymers could show behavior ranging from thermoplastics to thermoplastic elastomers, with the highest tensile strength of 13 MPa or elongation at break of 1424%. Furthermore, mechanical properties of these triblock copolymers could be easily manipulated by adjusting the molecular mass of the PI midblock. This efficient, facile and mild synthesis method in this work can be further applied to develop more environment-friendly elastomers with desired mechanical properties.