Thermal, electrical and rheological behavior of high-density polyethylene/graphite composites
作者：Wei Luo, Cheng Cheng, Shengtai Zhou, Huawei Zou*,
關鍵字：Thermal conductivity · High-density, polyethylene, Expandable graphite, Flake graphite, Polymer-matrix composites
論文來源：期刊
具體來源：Iran Polymer Journal, 2015, 24(7): 573-581.
發表時間：2015年
Abstract: Thermally conductive high-density polyethylene (HDPE) composites with high loadings of flake graphite (FG) and expandable graphite (EG) were prepared by melt-blending process. Thermal conductivity of the composites was measured by hot disk method, and a very high value of 13.41 W/mK was obtained for HDPE/EG composite with 60 wt% EG, which is 28.3 times and 60.4 % higher than the values obtained for the HDPE and an HDPE/FG system with 60 wt% FG, respectively. Twopoint method was applied to evaluate the electrical conductivity of the composites with various graphite loadings, and thermal percolation was observed in the vicinity of the electrical percolation threshold concentration. Dynamic rheology analysis was employed to define the geometrical changes caused by the interconnection of the inorganic fillers. The results showed that the in situ exfoliation of EG during the blending process could form more effective conductive pathways than those of FG-filled composites at the same graphite loadings. Such kind of pathways was responsible for the substantial improvement of the overall thermal and electrical conductivity of HDPE/EG composites. The results of dynamic rheology also confirmed that the thermally conductive networks were primarily formed at approximately 20 and 40 wt% of graphite concentrations for HDPE/EG and HDPE/FG composites, respectively.